Eds analysis company by MicroVision Laboratories, Inc. in 2021? Approach: MicroVision Labs’ staff consulted with the client, and determined that, unfortunately, there could be a number of potential sources of a white material. Even before the bottle with the suspended material arrived, it was determined that there was less than 50 mL of water remaining, and likely less than a gram of material suspended in the water. The client was aware that this material could represent precipitated minerals from the source water, a polymer residue from the bottles, some form of biological tissue that might have formed despite sterilization procedures, or could very well represent some completely unforeseen foreign material. The issue facing the client is how to have the material tested, as most tests that they might request for one or the other of these known potential sources would destroy or alter the sample. Choosing a test was therefore something of a gamble, because if they tested for calcium (mineral precipitate) and it came up negative – that didn’t actually tell them what the powder was, just that it didn’t have any calcium. Based on this conversation, the non-destructive, specialized testing at MicroVision Laboratories was chosen as the best choice.
MicroVision Labs uses a brand new comprehensive LUMOS micro-IR that combines standard optical and polarized light microscopy. It also has sophisticated automation for a variety of IR spectral measurement techniques. Our LUMOS system is the first of its kind to be commissioned in the US and allows for particles down to 5um in diameter to be examined. This new instrument increases our ability to provide quality organic spectroscopy and enables sample mapping using special IR features with full automation for feature identification with quantifiable, traceable spectral measurement.
What is your standard turnaround time (TAT) and can it be expedited? Our standard TAT is 5 to 10 business days. We can provide faster TATs on request with the following surcharges: – Same day to 24 hour rush is 100% surcharge – 2 day rush is 75% surcharge – 3 day rush is 50% surcharge – 4 day rush is 25% surcharge Rush requests must have prior approval otherwise we cannot guarantee turnaround times. Find a few more details on top light microscopy labs. We are proud to announce that MicroVision Labs is now accredited to the ISO/IEC 17025:2017 standard. This represents over a year of diligent effort from all of our staff to verify and validate our in house SOP’s and transform our quality management system to one that is compliant to this international standard. This certification requires that accredited labs demonstrate that they are competent and can produce technically valid data and results unlike other certifications such as ISO 9001:2015. This represents an obvious value to our clients.
An affected floor tile was submitted to determine if the previous mold testing had missed a source on the tile backing or mastic. Additionally, a new tile from the same manufacturing lot was submitted for comparison. The process of preparing and examining the sample and reference tile was documented. Areas with darkened surface features were imaged and then cut out and examined. While the dark spots looked very discrete when examined by eye, under top light polarized microscopy they appeared more diffuse at the outer edges. The darkest areas surrounded what appeared to be particles embedded in the surface.
Close examination of any possible defects or voids was undertaken at higher magnification. The voids did not appear to create any structural or conductivity issues. Additionally, the formation and contiguity of intermetallic bonds between the contacts and solder were shown using a combination of EDS line scan elemental spectroscopy and elemental mapping. The SEM image and the EDS map to the left show the intermetallic layer between the copper wire and the tin/lead solder via the mixture of the red copper and the blue tin. Find additional info on this website.